How to increase your coating material yield in sputtering
Investigation of Titanium target pieces for PVD sputtering
After using Titanium Grade 2 we faced different erosion profiles and obvious the material seems to have also different grain size
Preparation: US cleaning in 2-Propanol, Cross section through the sputter groove
Method: Scanning Electron Microscope LEO 1530 VP| Light Optical Microscope Olympus BX51, digital imaging Keyence VHX 700
The sputter profile after end of use had big visible differences
Fig. 1 The 3 target pieces, obviously coarse grained on the left side, medium sized and fine grained right hand side
Fig. 2 The 3 target pieces cut for examinations – higher magnified the striking difference of grain size
Scanning Electron Microscopy – Comparison
Fig. 3 Sputtered surface fine graines
Fig 4 Sputtered surface medium grain size
Fig. 5 Sputtered surface coarse graines
The fine grained sample shows a quite unusual small grain size of 33 µm. Additionally the macro-structure reveals a residue cold working texture parallel to the flat target plane. The medium size grain sample exhibits a quite uniform grain distribution of about 121 µm. Residue cold working patterns disappeared.
The coarse grain size sample shows the big grains, locally more than 1 mm in diameter
a few millimeters beneath the sputter surface. Towards the cooled back side (bottom) of the target, the grain size ranges comparable with the medium grain size sample.
These findings can be explained as follows:
The as received condition of the target material shows a very fine grain size and still cold working texture patterns.
Presumably the target material was not enough heat treated after the last milling step.